| Material: | |
|---|---|
| Color: | |
| Brand: | |
| Availability: | |
| Quantity: | |
02A045
HaoRui
02A045
Radial slot pattern and centre bore made to drawing
Flatness and parallelism lapped to a few microns
Compressive strength 3000 MPa - no deformation under press load
No rust and no cold welding to the workpiece
Diamond-ground working faces for a smooth release
Pressing and stamping tooling
Tablet and pellet forming
Powder compaction dies
Food and pharma contact parts
Wear plates in presses
| Property | Item | 3Y-TZP White / Black | Mg-PSZ Gold yellow | Nano 3Y-TZP Blue |
|---|---|---|---|---|
| Mechanical | Colour | Ivory / Black | Gold yellow | Nano blue |
| Density | 6.02 g/cm3 | 5.7 g/cm3 | 6.01 g/cm3 | |
| Bending strength | 800 MPa | 450 MPa | 1200 MPa | |
| Compressive strength | 3000 MPa | 2500 MPa | 3000 MPa | |
| Elastic modulus | 200 GPa | 250 GPa | 220 GPa | |
| Fracture toughness | 8 MPa m1/2 | 6-7 MPa m1/2 | 14 MPa m1/2 | |
| Weibull coefficient | 15 m | 12 m | 25 m | |
| Vickers hardness | 1200 HV0.5 | 1100 HV0.5 | 1200 HV0.5 | |
| Thermal | Coeff. of linear thermal expansion | 10 x10-6/K | 10 x10-6/K | 10 x10-6/K |
| Thermal conductivity | 3 W/mK | 3 W/mK | 2 W/mK | |
| Thermal shock resistance | 300 dT degC | 450 dT degC | 300 dT degC | |
| Max working temperature | 1000 degC | 2100 degC | 1000 degC | |
| Electrical | Volume resistance at 20degC | >10^13 Ohm cm | >10^14 Ohm cm | >10^13 Ohm cm |
Standard properties of the zirconia grades we machine. Tolerances, surface finish and part-specific dimensions are made to your drawing.
Send a drawing (STEP / DXF / PDF) or a sample - we quote from either.
Material: white 3Y-TZP, anti-static black 3Y-TZP, nano-tough blue 3Y-TZP or yellow Mg-PSZ.
Tolerance: +/-0.01 mm typical, down to +/-0.005 mm on critical dimensions.
Finishing: as-machined, diamond-ground, lapped or mirror-polished.
Prototype and small batch orders accepted; production quantities supplied with inspection report on request.
Quality you can verify: Haorui Industrial operates an ISO 9001:2015 certified quality management system (scope: production and sales of precision mechanical ceramics parts), and our yttria-stabilized zirconia ceramics are RoHS 2.0 compliant - tested per IEC 62321 by an accredited third-party laboratory (Shenzhen United Testing). We exhibit every year at CIOE (China International Optoelectronic Exposition) and semiconductor industry expositions in Shenzhen - visit our booth to see the parts in person.