| Property | Item | 3Y-TZP White /Black | Mg-PSZ | Nano 3Y-TZP | |||
| Mechanical Characteristics | Color | Ivory/Black | - | Gold Yellow | - | BLUE | - |
| Density | 6.02 | g/cm3 | 5.7 | g/cm3 | 6.01 | g/cm3 | |
| Bending Strength | 800 | MPa | 450 | MPa | 1200 | MPa | |
| Compressive trength | 3000 | MPa | 2500 | MPa | 3000 | MPa | |
| Elastic Modulus | 200 | GPa | 250 | GPa | 220 | GPa | |
| Fracture Toughness | 8 | MPa m1/2 | 6~7 | MPa m1/2 | 14 | MPa m1/2 | |
| Weber Coefficient | 15 | m | 12 | m | 25 | m | |
| Vickers Hardness | 1200 | HV 0.5 | 1100 | HV 0.5 | 1200 | HV 0.5 | |
| Thermal Characterics | Coefficient of Line Thermal Expansion | 10 | 10-6K-1 | 10 | 10-6K-1 | 10 | 10-6K-1 |
| Thermal Conductivity | 3 | W/mK | 3 | W/mK | 2 | W/mK | |
| Thermal Shock Resistance(Put in Water) | 300 | ΔT °C | 450 | ΔT °C | 300 | ΔT °C | |
| Max Working Temperature | 1000 | °C | 2100 | °C | 1000 | °C | |
| Electrical Characteristics | Volume Resistance at 20°C | >1013 | Ωcm | >1014 | Ωcm | >1013 | Ωcm |
| Dielectric Strength | 11×106 | V/m | 13 × 105 | V/m | 11×106 | V/m | |
| Dielectric Constant | 33 | εr | 28 | εr | 33 | εr | |
| One MHZ Dielectric Loss Angle at 20°C | 0.0016 | tanδ | 0.0017 | tanδ | 0.0016 | tanδ | |
| Chemical Characteristics | Nitric Acid (60%) 90°C | ≒0.00 | WT Loss mg/cm2/day | 0.1 | WT Loss mg/cm2/day | ≒0.00 | WT Loss mg/cm2/day |
| Sulphuric Acid (95%) 95°C | 0.04 | 0.34 | 0.03 | ||||
| Caustic Soda (30%) 80°C | 0.08 | 0.95 | 0.06 | ||||
This data is the result of laboratory testing. Customers need to judge whether it can be used according to the specific environment. | |||||||
| Property | Item | 3Y-TZP White /Black | Mg-PSZ | Nano 3Y-TZP | |||
| Mechanical Characteristics | Color | Ivory/Black | - | Gold Yellow | - | BLUE | - |
| Density | 6.02 | g/cm3 | 5.7 | g/cm3 | 6.01 | g/cm3 | |
| Bending Strength | 800 | MPa | 450 | MPa | 1200 | MPa | |
| Compressive trength | 3000 | MPa | 2500 | MPa | 3000 | MPa | |
| Elastic Modulus | 200 | GPa | 250 | GPa | 220 | GPa | |
| Fracture Toughness | 8 | MPa m1/2 | 6~7 | MPa m1/2 | 14 | MPa m1/2 | |
| Weber Coefficient | 15 | m | 12 | m | 25 | m | |
| Vickers Hardness | 1200 | HV 0.5 | 1100 | HV 0.5 | 1200 | HV 0.5 | |
| Thermal Characterics | Coefficient of Line Thermal Expansion | 10 | 10-6K-1 | 10 | 10-6K-1 | 10 | 10-6K-1 |
| Thermal Conductivity | 3 | W/mK | 3 | W/mK | 2 | W/mK | |
| Thermal Shock Resistance(Put in Water) | 300 | ΔT °C | 450 | ΔT °C | 300 | ΔT °C | |
| Max Working Temperature | 1000 | °C | 2100 | °C | 1000 | °C | |
| Electrical Characteristics | Volume Resistance at 20°C | >1013 | Ωcm | >1014 | Ωcm | >1013 | Ωcm |
| Dielectric Strength | 11×106 | V/m | 13 × 105 | V/m | 11×106 | V/m | |
| Dielectric Constant | 33 | εr | 28 | εr | 33 | εr | |
| One MHZ Dielectric Loss Angle at 20°C | 0.0016 | tanδ | 0.0017 | tanδ | 0.0016 | tanδ | |
| Chemical Characteristics | Nitric Acid (60%) 90°C | ≒0.00 | WT Loss mg/cm2/day | 0.1 | WT Loss mg/cm2/day | ≒0.00 | WT Loss mg/cm2/day |
| Sulphuric Acid (95%) 95°C | 0.04 | 0.34 | 0.03 | ||||
| Caustic Soda (30%) 80°C | 0.08 | 0.95 | 0.06 | ||||
This data is the result of laboratory testing. Customers need to judge whether it can be used according to the specific environment. | |||||||