Customised Microporous (porous ceramics) Ceramic Suction Cup Precision ground parts

Name: Customised Microporous (porous ceramics) Ceramic Suction Cup Precision ground parts
Brand: HaoRui
Rating: 5.0 (85 reviews)

Resistant to high temperature, abrasion, chemical corrosion,

high mechanical strength,

easy to regenerate and excellent thermal shock resistance.

Availability:

Quantity:



Inquire Add to Basket

Model:
05A02
Brand:
HaoRui
Code:
custom01001

Product Description

Welcome to visit Shenzhen Haorui Industrial Technology Co., Ltd. and we hope our products will be of interest to you!

Founded in June 2006, the company is a professional enterprise specialising in the research, development, manufacture and sales of non-standard industrial ceramics, cemented carbide (tungsten steel), and all kinds of metallic and non-metallic precision mechanical parts.

After more than 15 years of development, we have accumulated rich experience in the industry and cultivated a group of professional technicians. We have a perfect production process and quality management system, as well

as a set of precision machining equipment and testing equipment. At present, we have more than 3,000 customers at home and abroad, and have cooperated with more than 30 colleges and research institutes, and have a high reputation and good word of mouth in the same industry, the company's overall strength is in the leading position in the industry.

Microporous ceramic suction cups are mainly used in the semiconductor industry as a fixture for wafer transport and cleaning, while it also has a wide range of applications in medical and other fields. Microporous ceramic suction cups are generally made of ceramic materials with 1um, 5um-100um pore size, and this special porous ceramic has the characteristics of uniform pore distribution and wear resistance. SHENZHEN HAORUI Ceramics has long been committed to the production of high-quality microporous ceramic suction cups, which can replace the domestic products of the same level.

Processing accuracy:
(1) shaft: roundness 0.002 mm, concentricity 0.002 mm, finish Ra0.1 ;
(2) Hole: minimum processing hole diameter 0.2 mm, depth up to 6 mm (depending on the material);
(3) groove (seam): minimum processing 0.1mm narrow groove, as well as a variety of shapes of the groove;
(4) plane: the minimum thickness of 0.1MM sheet can be processed, parallelism 0.001mm, measurement tolerance 0.001 mm, finish Ra0.1;
(5) Thread: the minimum can be processed M2 internal thread, precision GB-7h, external thread size is not limited, precision GB-6g.

Material properties:

Property	95%Al2O3	99%Al2O3	Zirconia Ceramics	Silicon carbide (SiC)	Silicon nitride (Si3N4)	Aluminum Nitride (AlN)	Machinable ceramics
colour	White	Light yellow	White	Black	Black	Grey	White
Density g/cm3	3.7g/cm³	3.9g/cm³	6.02g/cm³	3.2g/cm³	3.25g/cm³	3.2g/cm³	2.48g/cm³
water absorption	0 %	0 %	0 %	0 %	0 %	0 %	0 %
Hardness (HV)	23.7	23.7	16.5	33	20	-	-
Flexural strength (MPa)	300MPa	400MPa	1100MPa	450MPa	800MPa	310MPa	91MPa
Compressive strength (MPa)	2500MPa	2800MPa	3600MPa	2000MPa	2600MPa	-	340MPa
Young's modulus of elasticity	300GPa	300GPa	320GPa	450GPa	290GPa	310~350GPa	65GPa
heat conductivity	20W/m°C	32W/m°C	3W/m°C	50W/m°C	25W/m°C	150W/m°C	1.46W/m°C
dielectric strength	14KV/mm	14KV/mm	14KV/mm	14KV/mm	14KV/mm	14KV/mm	14KV/mm
Volume resistivity (25°C)	>10¹⁴Ω·cm	>10¹⁴Ω·cm	>10¹⁴Ω·cm	>10⁵Ω·cm	>10¹⁴Ω·cm	>10¹⁴Ω·cm	>10¹⁴Ω·cm
This data is typical of laboratory tests and the actual characteristics of specific production lots may vary.

Product customisation:

Non-standard parts customisation, due to the different requirements of product size, material material, processing accuracy, etc., resulting in material costs, processing costs, packaging logistics and other costs will be different. When ordering, please be sure to contact customer service, as much as possible to provide information about the parts (drawings or samples, use of the environment, etc.) and your requirements (quantity, delivery date, etc.), our company will recommend you to meet your requirements of the product programme and quotation.