Customized CNC Alumina Machining Ceramic Parts and Components intricately formed shapes

  • Very good electrical insulation.
  • Moderate to extremely high mechanical strength.
  • Very high compressive strength.
  • High hardness.
  • Moderate thermal conductivity.
  • High corrosion and wear resistance.
  • Good gliding properties.
  • Low density.
  • Operating temperature without mechanical load 1,000 to 1,700°C.
  • Bioinert and food compatible.
Availability:
Quantity:
  • 01057

  • HaoRui

  • custom01001

99 Alumina Ceramic Custom Finishing


CNC Machining of Aluminum Oxide Ceramic Part


CNC (Computer Numerical Control) machining is a subtractive manufacturing process that uses computer-controlled machinery to remove material from a workpiece to create a desired shape. When it comes to aluminum oxide ceramic parts, CNC machining offers several advantages over traditional manufacturing methods.


SHENZHEN HAORUI INDUSTRIAL specializes in providing a diverse selection of machined industrial ceramics across a broad spectrum of ceramic materials, ranging from machining blanks to intricately formed shapes. The precision machining of ceramics allows for the creation of components with exceptionally tight tolerances, ensuring high-quality results. Moreover, this process offers the capability to achieve superb surface finishes, meeting various business needs efficiently. Whether it is for prototype development or large-scale production, SHENZHEN HAORUI INDUSTRIAL is equipped to handle a wide range of projects with precision and expertise.



Properties of Alumina material (Al2O3)


Property
Item
95% Al2O3
99% Al2O3
99.8%Al2O3
Unit
Mechanical Characteristics
Color
White
light yellow
Ivory

Bulk Density
3.7
3.85
3.93
g/cm3
Water Absorption
0
0
0
%
Bending Strength
300
310
370
MPa
Compressive Trength
2,300
2,400
2500
MPa
Elastic Modulus
320
340
390
GPa
Fracture Toughness
3~4
3~4
4
MPa m1/2
Weber Coefficient
12
12
12
m
Vickers Hardness
1,400
1,600
1850
HV 0.5
Thermal Characterics
Coefficient of Line Thermal
Expansion
7~8
7~8
7~8
10-6 K-1
Thermal Conductivity
20
29
32
W/mK
Thermal Shock Resistance
(Put in Water)
250
200
280
ΔT °C
Max Working Temperature
1,500
1,600
1700
°C
Electrical Characteristics
Volume Resistance At 20°C
>1014
>1014
>1014
Ωcm
Dielectric Strength
15×106
15×106
15×106
V/m
Dielectric Constant
9
10
10
εr
One MHZ Dielectric Loss Angle
at 20°C
0.0004
0.0002
0.0001
tanδ
Chemical Characteristics
Nitric Acid (60%) 90°C
0.1
0.1
0.05
24H WT Loss mg/cm2
Sulphuric Acid (95%) 95°C
0.3
0.34
0.22
Caustic Soda (30%) 80°C
0.9
0.95
0.04


Previous: 
Next: 

Related Products

Leave a Message
Contact Us
Founded in June 2006, Shenzhen Haorui IndustriaI Technology Co.,Ltd. is a professional enterprise engaged in R&D, manufacturing and sales of non-standard industrial ceramics, hard alloys (tungsten steel) and various metal and non-metal precision machinery parts.

Quick Links

Product Category

Contact Us
Copyright © 2022 Shenzhen Haorui IndustriaI Technology Co.,Ltd. All rights reserved. Privacy Policy | Sitemap | Support By Leadong